Local Structure of Cerium in Aluminophosphate and Silicophosphate Glasses
2011
The local structure of cerium in two systematic compositional series of glasses, nominally CeP{sub 3}O{sub 9}-AlP{sub 3}O{sub 9} and CeP{sub 3}O{sub 9}-SiP{sub 2}O{sub 7}, was interrogated using X-ray photoelectron spectroscopy (XPS) and X-ray absorption fine structure (XAFS) spectroscopy. XPS revealed that, for glasses melted in air, {>=}95% of cerium ions are Ce{sup 3+}. This was independently confirmed using X-ray absorption near edge spectroscopy (XANES). Ce K-edge extended X-ray absorption fine structure (EXAFS) has been used to determine the local structure of Ce{sup 3+}. Near the metaphosphate composition, cerium was found to have an average cerium coordination number of {approx}7.0 and an average cerium-oxygen bond length of 2.41 {angstrom}. The average cerium coordination number and average cerium-oxygen bond distance were found to increase with decreasing cerium concentration in both compositional series. Rare-earth clustering is suggested based on numerical calculations for glasses containing {>=}14 and {>=}15 mol% Ce{sub 2}O{sub 3} for the aluminophosphate and silicophosphate series, respectively.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
47
References
25
Citations
NaN
KQI