Plasma treatment on SiO2f/SiO2 composites for their assisted brazing with Nb

Abstract Brazing SiO 2f /SiO 2 composites with metals is often associated with the problems of poor wettability with active brazing alloy and poor mechanical properties of joints. To overcome these problems, we report the plasma treatment on SiO 2f /SiO 2 by PECVD for their assisted brazing with Nb. The O–Si–O bonding changed into Si–C bonding on the surface of SiO 2f /SiO 2 by the plasma treatment can improve the wettability of Ag–Cu–Ti brazing alloy on SiO 2f /SiO 2 . Furthermore, SiO 2f /SiO 2 after the plasma treatment can contribute to the infiltration of brazing alloy into SiO 2f /SiO 2 to form the pinning structure and reducing the residual stress, which could strengthen the joint. The obtained joint has a high shear strength of 60.5 MPa, approximately 11 times higher than that without plasma treatment.