Over Limit Oxygen Effect on Crack Propagation of WWER 440 RPV Steel in Primary Circuit Water

Experience with operating nuclear power plants worldwide reveals that many failures may be attributed to fatigue associated with mechanical loading due to vibration and with corrosion effect due to exposure to high-temperature environment. In order to clarify the simultaneous influence on reactor pressure vessel (RPV) material testing of ferritic steel 15Ch2MFA used for RPV of WWER 440 was performed at Nuclear Research Institute (NRI) autoclaves. Cyclic and constant loadings were applied to Compact Tension (CT) specimens in WWER primary water environment at 290°C and simultaneous effect of different oxygen levels (< 20 ppb, 200 ppb, 2000 ppb) on crack propagation has been evaluated. Obtained crack growth rates are compared with ASME XI Code and VERLIFE curves and crack behaviour is discussed.Copyright © 2009 by ASME