Thermal cycles, interface chemistry and optical performance of Mg/SiC multilayers

2008 
The interplay between optical performance and the thermally activated interface chemistry of periodic Mg/SiC multilayers designed for application at 30.4 nm are investigated by optical (hard X-ray, soft X-ray and ultraviolet ranges, i.e. from 0.154 to 30.4 nm) reflectivity and X-ray emission spectroscopy. The multilayers are prepared by magnetron sputtering and then annealed up to a temperature of 500 °C. Two clear changes take place in the multilayer upon annealing. At first, between 200 and 300 °C a strong decrease of the reflectivity is observed, due to the development of interfacial roughness following the crystallization of the Mg layers. No interfacial compound is detected. Then, between 350 and 400 °C there is formation of the Mg2Si magnesium silicide at the interfaces following the reaction between the Mg and SiC layers. This also leads to the almost total loss of reflectivity of the multilayer. Thus, this kind of multilayer is thermally stable only for application requiring no heating above 200 °C.
    • Correction
    • Source
    • Cite
    • Save
    • Machine Reading By IdeaReader
    20
    References
    27
    Citations
    NaN
    KQI
    []