Opacifiers on color stability of maxillofacial silicone under aging and Indian weathering conditions: An in vitro study.

STATEMENT OF PROBLEM Resistance to long-term color change is a desirable property for facial prosthetic elastomers. Evidence for the color stability of maxillofacial silicones under aging and hot and humid Indian weathering conditions is lacking. PURPOSE The purpose of this in vitro study was to evaluate the effect of adding opacifiers on the color stability of maxillofacial silicone under human aging and Indian weather conditions. MATERIAL AND METHODS A total of 93 specimen disks were obtained from the A-2186, platinum-based, room-temperature vulcanized, maxillofacial silicone elastomer by using a O30×6-mm stainless-steel die. The specimens were divided into 3 main groups (n=30), C (control), T (titanium dioxide), and B (barium sulfate), and 1 additional specimen (n=1) from each group was stored in a closed box and further subgrouped as outdoor weathering (COut, TOut, BOut), acidic perspiration (CAcid, TAcid, BAcid), sebum (CSebum, TSebum, BSebum) (n=10), and visual comparison (CVis, TVis, BVis) (n=1). Baseline L∗, a∗, b∗ values were recorded by using a spectrophotometer and visual perception. The specimens were subjected to human and extraoral aging conditions, and the values were recorded again after 6 months. Data were analyzed statistically by using analysis of variance (ANOVA) and post hoc analysis with the Tukey post hoc test. RESULTS In group C, the mean color change for COut was 3.69 ±0.49; CAcid, 3.58 ±0.68; and CSebum, 7.53 ±0.22 (P<.001). In group T, the mean color change for TOut was 2.60 ±0.24; TAcid, 2.35 ±0.13; and TSebum, 4.91 ±0.44 (P<.001). In group B, BOut was 1.59 ±0.28, BAcid was 1.46 ±0.28, and BSebum was 4.03 ±0.71 (P<.001). The specimens containing barium sulfate showed the maximum color stability. The least color stability was observed in all specimens exposed to sebum solution and was significantly different (P<.001) from the outdoor weather and acidic perspiration specimens. Visually perceivable color changes were observed in specimens exposed to the sebum solution. CONCLUSIONS The addition of titanium dioxide and barium sulfate as opacifiers resulted in clinically acceptable color change when exposed to outdoor weathering and acidic perspiration but not in sebum solution.