Smart meta-superconductor MgB 2 constructed by the dopant phase of luminescent nanocomposite

On the basis of the idea that the injecting energy will improve the conditions for the formation of Cooper pairs, a smart meta-superconductor (SMSC) was prepared by doping luminescent nanocomposite Y2O3:Eu3+/Ag in MgB2. To improve the superconducting transition temperature (TC) of the MgB2-based superconductor, two types of Y2O3:Eu3+/Ag, which has the strong luminescence characteristic, with different sizes were prepared and marked as m-Y2O3:Eu3+/Ag and n-Y2O3:Eu3+/Ag. MgB2 SMSC was prepared through an ex situ process. Results show that when the dopant content was fixed at 2.0 wt.%, the TC of MgB2 SMSC increased initially then decreased with the increase in the Ag content in the dopant. When the Ag content is 5%, the TC of MgB2 SMSC was 37.2–38.0 K, which was similar to that of pure MgB2. Meanwhile, the TC of MgB2 SMSC doped with n-Y2O3:Eu3+/Ag increased initially then decreased basically with the increase in the content of n-Y2O3:Eu3+/Ag, in which the Ag content is fixed at 5%. The TC of MgB2 SMSC doped with 0.5 wt.% n-Y2O3:Eu3+/Ag was 37.6–38.4 K, which was 0.4 K higher than that of pure MgB2. It is thought that the doping luminescent nanocomposite into the superconductor is a new means to improve the TC of SMSC.