Fatigue strength of crack‐healed Si3N4/SiC composite ceramics

Si 3 N 4 /SiC composite ceramics were sintered and subjected to three-point bending on specimens made according to the appropriate JIS standard. A semi-circular surface crack of 110 μm in diameter was made on each specimen. By using three kinds of specimen (smooth, cracked and crack healed), crack-healing behaviour, cyclic and static fatigue strengths were determined systematically at room temperature and 1000°C. The main conclusions are as follows: (i) Si 3 N 4 /SiC composite ceramics have the ability to heal after cracking; (ii) crack-healed specimens showed similar cyclic and static fatigue strengths as smooth specimens, this being caused by crack healing; (iii) crack-healed zones had a sufficient fatigue strength and most fractures occurred outside the pre-cracked zone in those crack-healed specimens.