Expanding the Group of Porous Interpenetrated Zr-Organic Frameworks (PIZOFs) with Linkers of Different Lengths

A Zr-based MOF of the PIZOF type, which consists of two independent and mutually interpenetrating UiO-type frameworks with [Zr6O4(OH)4(O2C)12] nodes, does not only form with a PEPEP dicarboxylic acid (P = phenylene, E = ethynylene). Also dicarboxylic acids with the shorter PPPP and PEPP spacers were found to give PIZOFs, denoted PPPP-PIZOF and PEPP-PIZOF, respectively. Reducing the spacer length even further to a PEEP segment caused a switchover to the formation of a UiO framework. The hysteresis in the Ar sorption curve of PEPP-PIZOF-1 and the slightly too large amount of combustion residue from PPPP-PIZOF-1 suggest structural defects. These hint at a mismatch between the requirement of the optimal linker length for PIZOF formation and the lengths of the PEPP and PPPP dicarboxylates. Nevertheless, these dicarboxylates prefer the formation of a PIZOF over the formation of a UiO structure. PEPEP-PIZOF-2, PPPP-PIZOF-1, and PEPP-PIZOF-1 are stable in air up to 325, 350, and 300 °C, respectively, and have BET...