Interfacial Growth of TiO2-rGO Composite by Pickering Emulsion for Photocatalytic Degradation

A 2D sandwich-like TiO2-rGO composite was fabricated by the Pickering emulsion approach to improve the photocatalytic efficiency. Through an in situ growth of antase-TiO2 nanoparticles on the interface of O/W type GO Pickering emulsion, TiO2 nanoparticles were closely and densely packed on the surface of well-exfoliated rGO sheets; meanwhile, many mesoporous voids acting as the adsorption chamber and microreactor were produced. Evaluated by methylene blue (MB) degradation, its photocatalytic activity was prominent compared with the common TiO2-based photocatalyst, with the rate constants 5 and 3.1 times higher under visible light and xenon lamp, respectively. When we applied it in the photocatalytic degradation of tetracycline hydrochloride (TCH, such as 10 ppm) under the visible light without adding any oxidants, the total removal efficiency was as high as 94% after 40 min. The mechanism of this good photocatalytic efficiency was illustrated by the scavenger trapping tests, which showed that this unique ...