Improvement of Corrosion Resistance of TiO2 Layers in Strong Acidic Solutions by Anodizing and Thermal Oxidation Treatment

By anodization and thermal oxidation at 600 °C, an oxide layer on Ti with excellent corrosion resistance in strong acid solutions was prepared. The structural properties of TiO2 films before and after thermal oxidation were investigated with methods of Scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XRD) and X-ray diffraction (XPS). The electrochemical characterization was recorded via electrochemical impedance spectroscopy, potentiodynamic polarization and Mott–Schottky methods. XRD results show that a duplex rutile/anatase structure formed after oxidation, and the amount of anatase phase increased as the treatment time was prolonged from 3 to 9 h. XPS analysis indicates that as the thermal oxidation time increased, more Ti vacancies were present in the titanium oxide films, with decreased donor concentration. Longer thermal oxidation promoted the formation of hydroxides of titanium on the surface, which is helpful to improve the passive ability of the film. The anodized and thermally oxidized Ti samples showed relatively high corrosion resistance in 4 M HCl and 4 M H2SO4 solutions at 100 ± 5 °C. The passive current density values of the thermally oxidized samples were five orders of magnitude under the testing condition compared with that of the anodized sample. With the oxidation time prolonged, the passive current density decreased further to some extent.