Thermal and irradiation induced interdiffusion in Fe3O4/MgO(0 0 1) thin film
2009
Abstract The interface reactions in an epitaxial 10 nm-thick Fe 3 O 4 /MgO(0 0 1) film were investigated by using Rutherford Backscattering spectrometry (RBS), channeling (RBS-C) and X-ray reflectometry (XRR). The as-grown film had a good crystallinity indicated by the minimum yield and the half-angle value for Fe, respectively, χ min (Fe) = 22% and ψ 1/2 (Fe) = 0.62°. Annealing the films under partial argon pressure up to 600 °C led to a large enhancement of Mg out-diffusion into the film forming a wustite-type phase, but the total layer thickness did not change much. Ion irradiation of the film by 1 MeV Ar ion beam caused a strong Fe ion mixing resulting in a large interfacial zone with a thickness of 23 nm.