High quality uniform YBCO film growth by the metalorganic deposition using trifluoroacetates

Abstract A need exists for the large-area superconducting YBa 2 Cu 3 O 7-x (YBCO) films with high critical current density for microwave communication and/or electric power applications. Trifluoroacetic metalorganic (TFA-MOD) method is a promising low cost technique for large-scale production of YBCO films, because it does not need high vacuum device and is easily applicable to substrates of various shape and size. In this paper, double-sided YBCO films with maximum 2 in diameter were prepared on LaAlO 3 substrates by TFA-MOD method. Inductive critical current densitiy J c , microwave surface resistance R s , as well as the microstructure were characterized. A newly homemade furnace system was used to epitaxially grown YBCO films, which can improve the uniformity of YBCO film significantly by gas supply and temperature distribution proper design. Results showed that the large area YBCO films were very uniform in microstructure and thickness distribution, an average inductive J c in excess of 6 MA/cm 2 with uniform distribution, and low R s (10 GHz) below 0.3 mΩ at 77 K were obtained. Andthe film filter may be prepared to work at temperatures lower than 74 K. These results are very close to the highest value of YBCO films made by conventional vacuum method, so we show a very promising route for large-scale production of high quality large-area YBCO superconducting films at a lower cost.