Preparation and characterization of poly (N-isopropylacrylamide-co-dimethylaminoethyl methacrylate) microgel latexes

Monodisperse cationic thermosensitive latex microgels have been prepared by radical-initiated precipitation polymerization of N-isopropylacrylamide, methylene bisacrylamide using 2,2′-azobis(2-amidinopropane hydrochloride) as an initiator and dimethylaminoethyl methacrylate (DMAEMA) as a cationic monomer. The final microgel latexes were characterized with respect to water-soluble polymer formation, particle size and size distribution. Adding cationic monomer (DMAEMA) was found to drastically affect the particle size, but not the size distribution as observed both by transmission electron microscopy and quasielastic light scattering (QELS). However, too high a DMAEMA concentration in the feed composition led to enhanced formation of water-soluble polymer. The volume phase-transition temperature of cleaned microgels examined by QELS (particle size versus temperature) was found to be around 32 °C and was slightly dependent on the concentration of the cationic monomer. The volume phase-transition temperature range becomes broader with increasing cationic monomer concentration. In addition, the pH of the polymerization medium was found to affect the final particle size and amount of water-soluble polymer formed.