Fabrication and orientation control of highly cation-ordered epitaxial PbSc0.5Ta0.5O3 thin films on Si (100)

Highly cation-ordered (100) and (110)-oriented PbSc0.5Ta0.5O3 (PST) films were deposited on buffered Si (100) substrates using pulsed laser deposition. Switching of crystal orientation from (100) to (110) was achieved by replacing the Si (100)/ZrO2:Y2O3 (100)/CeO2 (100)/LaNiO3 (100)/PST (100) heterostructure with Si (100)/ZrO2:Y2O3 (YSZ) (100)/SrRuO3 (110)/PST (110). The out-of-plane and in-plane crystal orientation and internal microstructure of (001) and (110) PST films were analyzed in detail by X-ray diffraction, pole figure measurements, and transmission electron microscopy. XRD superstructure reflections indicate that both (100) and (110) PST films are highly cation-ordered and transmission electron microscopy measurements show nano-domains of 15 nm size. The electrical measurements show that the PST films are ferroelectric and that the ferroelectric properties are linked to the microstructure. We have demonstrated the successful integration of PST films on Si substrates with control on growth orien...