Impurity effects in neutron-irradiated simple oxides: Implications for fusion devices

Abstract Radiation damage induced by neutron irradiation was studied in undoped MgO crystals and in MgO doped with either iron, hydrogen or lithium impurities. The oxygen-vacancy concentration produced by irradiation increases with neutron fluence. The net production rates resulting from irradiations with 14.8 MeV neutrons are about twice those produced by fission neutrons. In nominally pure crystals, the oxygen-vacancy concentration incurred by the fission-neutron irradiation is higher in crystals with a larger number of inherent impurities (such as iron) due to trapping of interstitials by impurities. Suppression of these defects is observed in MgO:H crystals and attributed to migration of oxygen vacancies to microcavities filled with H 2 gas. In MgO:Li crystals irradiated with neutron fluences below 10 18  n/cm 2 , most of the oxygen vacancies are camouflaged as hydride ions. Nanoindentation experiments show that hardness increases with neutron fluence and is independent of the presence of lithium in the crystal. Comparison between a neutron-irradiated and a thermochemically reduced crystal containing similar concentrations of oxygen vacancies shows that 70% of the neutron-irradiation hardening is produced by interstitials, 30% by oxygen vacancies and a negligible amount by higher-order point defects.