Molecular-beam epitaxial growth of tensile-strained and n-doped Ge/Si(001) films using a GaP decomposition source
2014
Abstract We have combined numerous characterization techniques to investigate the growth of tensile-strained and n -doped Ge films on Si(001) substrates by means of solid-source molecular-beam epitaxy. The Ge growth was carried out using a two-step growth method: a low-temperature growth to produce strain relaxed and smooth buffer layers, followed by a high-temperature growth to get high crystalline quality Ge layers. It is shown that the Ge/Si Stranski–Krastanov growth mode can be completely suppressed when the growth is performed at substrate temperatures ranging between 260 °C and 300 °C. X-ray diffraction measurements indicate that the Ge films grown at temperatures of 700–770 °C are tensile-strained with typical values lying in the range of 0.22–0.24%. Cyclic annealing allows further increase in the tensile strain up to 0.30%, which represents the highest value ever reported in the Ge/Si system. n -Doping of Ge was carried out using a GaP decomposition source. It is shown that heavy n -doping levels are obtained at low substrate temperatures (210–250 °C). For a GaP source temperature of 725 °C and a substrate temperature of 210 °C, a phosphorus concentration of about 10 19 cm − 3 can be obtained. Photoluminescence measurements reveal an intensity enhancement of about 16 times of the direct band gap emission and display a redshift of 25 meV that can be attributed to band gap narrowing due to a high n -doping level. Finally, we discuss about growth strategies allowing optimizing the Ge growth/doping process for optoelectronic applications.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
26
References
18
Citations
NaN
KQI