Highly transparent nanocomposites based on poly(vinyl alcohol) and sulfated UV-absorbing wood nanofibers

Unbleached lignocellulose fibers were investigated for the fabrication of wood-based UV-absorbing nanofibers and were used to produce transparent nanocomposites. Groundwood pulp (GWP) and sawdust were selected as raw materials thanks to their low processing degree of fibers and abundant availability as a low-value industrial side stream, respectively. Both materials were first sulfated using a reactive deep eutectic solvent. The sulfated wood and sawdust nanofibers (SWNFs and SSDNFs, respectively) were fabricated using a mild mechanical disintegration approach. As a reference material, sulfated cellulose nanofibers (SCNFs) were obtained from bleached cellulose pulp. Our results showed that both GWP and sawdust exhibited similar reactivity compared to bleached cellulose pulp, whereas the yields of sulfated lignin-containing pulps were notably higher. The diameters of both SWNFs and SSDNFs were approximately 3 nm, which was similar to the SCNFs. When 10 wt% of lignin-containing nanofibers were mixed togethe...