Formation and Structure of Highly Ordered Self-Assembled Monolayers by Adsorption of Acetyl-Protected Conjugated Thiols on Au(111) in Tetrabutylammonium Cyanide Solution

The surface structure and binding conditions of self-assembled monolayers (SAMs) on Au(111) derived from 1-acetylthio-4-[(phenyl)ethynyl]benzene (OPE2-SAc) without and with tetrabutylammonium cyanide (TBACN) as a deprotection reagent were examined using scanning tunneling microscopy (STM) and X-ray photoelectron spectroscopy (XPS). STM observation revealed that OPE2-S SAMs on Au(111) formed from direct adsorption of OPE2-SAc in 1 mM methanol solution at room temperature (RT) for 24 h were composed of short-range, ordered phase separated by a disordered phase. In contrast, adsorption of OPE2-SAc SAMs on Au(111) at a higher solution temperature of 50 °C for 24 h led to formation of a fully ordered phase with slightly increased domain size. The structural quality of OPE2-S SAMs on Au(111) was remarkably enhanced when TBACN was used. OPE2-S SAMs at RT had a well-ordered (√3 × √7)R30° structure with a domain size larger than 80 nm. The SAMs deposited at 50 °C contained very uniform and highly ordered domains w...