Methyl acrylate/N‐phenylmaleimide copolymers, 1. Synthesis of copolymers and effect of copolymer composition on huggins constant KH

This paper deals with the synthesis of methyl acrylate/N-phenylmaleimide copolymers having different compositions, (mole fractions of N-phenylmaleimide for the four copolymers MP-1, MP-2, MP-3, and MP-4 are 0.0664, 0.3905 and 0.5445, respectively) by free radical solution polymerization in cyclohexanone using azoisobutyronitrile as an initiator. The compositions of the copolymers have been determined by elemental analysis. The variation of the Huggins constant KH with composition for the copolymers in three solvents, methyl ethyl ketone, dimethylformamide and cyclohexanone is described. KH is found to be dependent both on solvent and composition of the copolymers. In dieser Arbeit wird die Herstellung von Methylacrylat/N-Phenylmaleimid-Co-polymeren verschiedener Zusammensetzung durch radikalische Polymerisation in Cyclohexanon mit Azoisobutyronitril als Initiator untersucht. Die Molenbruche fur N-Phenylmaleimid der vier Copolymeren MP-1, MP-2, MP-3 und MP-4 sind 0,0664,0,2344, 0,3905 und 0,5445. Die Zusammensetzung der Copolymeren wurde durch Elementaranalyse bestimmt. Weiter wird die anderung der Huggins-Konstante KH mit der Zusammensetzung fur die Copolymeren in den Losungsmitteln Dimethyl-formamid, Methylethylketon und Cyclohexanon beschrieben. KH hangt vom Losungsmittel und von der Zusammensetzung der Copolymeren ab.