Photocatalytic NO{sub x} abatement by calcium aluminate cements modified with TiO{sub 2}: Improved NO{sub 2} conversion

Photocatalytic activity of TiO{sub 2} was studied in two types of calcium aluminate cement (CAC) under two different curing regimes. The effect of the TiO{sub 2} addition on the setting time, consistency and mechanical properties of the CACs was evaluated. The abatement of gaseous pollutants (NO{sub x}) under UV irradiation was also assessed. These cementitious matrices were found to successfully retain NO{sub 2}: more abundant presence of aluminates in white cement (w-CAC, iron-lean) helped to better adsorb NO{sub 2}, thus improving the conversion performance of the catalyst resulting in a larger NO{sub x} removal under UV irradiation. As evidenced by XRD, SEM, EDAX and zeta potential analyses, the presence of ferrite in dark cement (d-CAC, iron-reach) induced a certain chemical interaction with TiO{sub 2}. The experimental findings suggest the formation of new iron titanate phases, namely pseudobrookite. The reduced band-gap energy of these compounds compared with that of TiO{sub 2} accounts for the photocatalytic activity of these samples.