High temperature oxidation of rapidly solidified alloys

Ductile and microcrystalline thin Fe-Cr-Al foils with an elevated aluminium content up to 12 wt.-% were produced by a rapid soldification process. Alloys with different compositions were tested in isothermal oxidation experiments (He-O2, p(O2) = 133 mbar, T = 1273 K) and in cyclic oxidation experiments (dry air). The rapidly solidified alloys show a better oxidation resistance compared to conventionally rolled material. Cerium addition to the alloy leads to an improved oxide adhesion onto the substrate. The oxidation resistance is further improved by increasing the aluminium and decreasing the chromium content of the alloy. Hochtemperaturoxidation schnellerstarrter Legierungen Dunne, mikrokristalline und duktile Fe-Cr-Al-Folien mit erhohtem Aluminiumgehalt bis 12 Gew.-% wurden durch rasche Erstarrung hergestellt. Legierungen mit verschiedener Zusammensetzung wurden in isothermen Oxidationsexperimenten (He-O2, p(O2) = 133 mbar, T = 1273 K) und in zyklischen Oxidationsexperimenten (in trockener Luft) untersucht. Die rasch erstarrten Legierungen zeigen im Vergleich zu konventionell gewalztem Material eine bessere Oxidationsbestandigkeit. Ein Cer-Zusatz zu der Legierung verbessert die Haftung des Oxids auf dem Substrat. Die Oxidationsbestandigkeit wird durch Erhohung des Aluminium- und Erniedrigung des Chromgehaltes der Legierung weiter verbessert.