Impregnation of poly(L-lactide- ran - δ -valerolactone) with essential bark oil using supercritical carbon dioxide

This work studied the incorporation of essential bark oil from Thujopsis dolabrata var. hondae, which is known to repel various insects, in poly(L-lactide-ran-δ-valerolactone) [poly(L-LA-ran-VL)] using supercritical carbon dioxide (scCO2). The poly(L-LA-ran-VL) was synthesized by first purifying the monomers by azeotropic distillation with benzene, followed by polymerization with Sn(oct)2 using the same equipment, representing an efficient one-pot process. The copolymerization of L-LA with VL using this technique at a feed ratio of 90/10 mol/mol gave poly(L-LA-ran-VL) (91/9) with a molecular weight of 6.48 × 104 g/mol and a high yield of 74.9%. Products with molecular weights over 5.0 × 104 g/mol were obtained at L-LA feed proportions of 70 to 90%. Impregnation trials were conducted between 40 and 120 °C at 14 MPa for 3 h. The oil content of a 73/27 specimen was found to increase significantly during processing at 100 or 120 °C. During enzymatic degradation with proteinase K, the 91/9 specimen showed the fastest degradation rate. Although the 71/29 sample was slowly hydrolyzed in a phosphate buffer at pH 7.0, the release of oil vapor from this material was slightly higher than that from the 91/9 specimen, and the vapor release rate continuously increased throughout the hydrolysis process.