Molecular level analyses of mechanical properties of PTFE sterilized by Co-60 γ-ray irradiation for clinical use

Abstract Recently, Co-60 gamma-ray irradiation has become markedly popular for the sterilization of biomedical materials, including expanded PTFE. However, its effect on the properties of PTFE has not been thoroughly examined. In this study, changes in the properties of PTFE before and after irradiation were analyzed physicochemically and discussed crystallographically. The tensile breaking strengths of PTFE decreased markedly on irradiation at 1 kGy, and were maintained at almost one fourth of the original value (44.3±2.5 N/mm 2 ) ranging from 5 to 100 kGy. XPS analysis indicated that the atomic concentrations of carbon (C) and fluorine (F) of PTFE were not different among samples irradiated at various dosages. Raman spectra of PTFE showed a slight increase of the absorption peak intensity at 735 cm –1 in an irradiation dosage-dependent manner. X-ray diffraction showed that the crystal size of PTFE (56.7±1.0 nm) became smaller after radiation at 100 kGy (48.5±0.6 nm). These results are consistent with the above results of Raman analysis. It is suggested that the observed changes in the mechanical properties of PTFE may be due to nano-scale C–C bond scission by gamma ray irradiation, and not due to the formation of micro-scale cracks.