Dynamic rheology behavior of electron beam-irradiated cellulose pulp/NMMO solution

Abstract The rheological behavior of irradiated cellulose pulp solution by electron beam was investigated. Storage modulus G ′, loss modulus G ″, the dependence of complex viscosity η * and frequency ω of cellulose solutions were measured by DSR-200 Rheometer (Rheometrics co., USA). The molecular weight of irradiated cellulose was measured via the intrinsic viscosity measurement using an Ubbelohde capillary viscometer. The crystalline structure was studied by FTIR Spectroscopy. The results congruously showed that the molecular weight of pulp cellulose decrease and the molecular weight distribution of cellulose become narrow with increase in the irradiation dose. Moreover, the crystalline structure of the cellulose was destroyed, the force of the snarl between the cellulose molecules weakens and the accessibility of pulp spinning is improved. The study supplies some useful data for spinnability of irradiated cellulose and technical data to the filature industry.