Surfactant and nano Aluminum PMEDM on Molybdenum High Speed Steel

Abstract This research study focused on the effect of surfactant and nano aluminum powder mixed electrical discharge machining dielectric (PMEDM) on surface roughness (Ra) and surface morphology of molybdenum high speed steel. Conventional machining of molybdenum high speed steel is a challenge even when employing non-conventional machining processes such as electrical discharge machining (EDM) due to surface alteration, low material removal rate and residual stress during the EDM process. PMEDM is a new developed and improved EDM process able to address some of the above mentioned drawbacks for industrial application. Variable parameters selected are peak-current, ON-time, gap voltage and nano aluminum concentration. Surfactant concentration remained constant. PMEDM although still in experimental stage has shown slight improvement in Ra and surface morphology. However, the effect of surfactant is not significant as expected. Keywords : EDM, Molybdenum high speed steel, surface roughness, surface morphology Resume Ce travail de recherche se focalise sur l’effet de surfactant et nano aluminium melanges au fluide dielectrique de machine electroerosion sur la rugosite et la surface morphologique de l’alliage d’acier a haute vitesse au molybdene. L’usinage conventionnel de l’alliage d’acier a haute vitesse au molybdene est un defi meme quand le procede non conventionnel d’usinage tel que l’electroerosion est employe et ceci est du a l’alteration de surface usinee et la contrainte residuelle durant l’usinage electroerosion. Nano metallique ajoute au fluide dielectrique de machine electroerosion est un nouveau developpement et amelioration de l’usinage electroerosion capable d’adresser quelques des problemes mentionnes ci-haut pour une application industrielle. Les parametres selectionnes sont le courant electrique, le voltage, le temps de decharge electrique par cycle et la concentration de nano aluminium. La concentration de surfactant reste constante. Malgre qu’une poudre metallique melangee au fluide dielectrique de machine electroerosion est au stage experimental, il y a quelque amelioration sur la rugosite et la morphologie de surface usinee. Cependant, l’effet de surfactant n’est pas significatif come attendu.   Mots cles : electroerosion, acier a haute vitesse au molybdene, rugosite, surface morphologique