Decontamination of rough titanium surfaces with diode lasers: microbiological findings on in vivo grown biofilms

Objectives: The bactericidal efficacy of diode lasers has already been demonstrated in vitro. We investigated the reduction of aerobe bacteria – colonizing rough titanium samples in biofilms intraorally grown – by diode lasers of different wave lengths. Material and methods: Twenty-two volunteers participated in the trial. They were fitted for 10 days with custom-made intraoral plastic splints carrying titanium sleeves. A part of the sleeves was then irradiated with diode lasers in different modes. The other part remained non-irradiated and served as control. Directly after irradiation, the sleeves were swabbed and the gained bacteria were first examined microscopically and then were cultured under aerobic conditions. Results: The bacteria in the controls and in the treated samples were quantified. A comparison with the controls revealed a marked overall reduction of bacterial colonization in all irradiated sleeves. Continuous irradiation for 20 s reduced bacteria counts by 99.67% at 810 nm and 99.58% at 980 nm. Repeating the 20 s exposure five times reduced counts by 99.98% at 810 nm and by 99.39% at 980 nm. A 98.86% reduction was seen after irradiation in pulsed mode. A further analysis in respect of different isolated bacteria revealed that the streptococci group was reduced by 99.29–99.99%, while the staphylococci group was reduced to a lesser extent in the range 94.67–99.99%. Conclusion: The results are of clinical relevance. In comparison with the mean bacterial counts of the untreated samples, all irradiation programs studied in this investigation reduced mean bacterial colonization in a biofilm on intraoral rough titanium surfaces by more than 98%. The actual extent of reduction was dependent on the bacteria species as well as on the irradiation mode.