Preservation of resin-dentin interfaces treated with benzalkonium chloride adhesive blends.

Reducing collagen degradation within hybrid layers may contribute to the preservation of adhesive interfaces. This study evaluated the stability of resin–dentin interfaces treated with benzalkonium chloride (BAC)-modified adhesive blends and assessed collagen degradation in dentin matrices treated with BAC. The etch-and-rinse adhesive, Adper Single Bond Plus, modified with 0.5% and 1.0% BAC, was evaluated for microtensile bond strength (μTBS) and nanoleakage (NL) after 24 h and 1 yr. Thirty completely demineralized dentin beams from human molars were dipped for 60 s in deionized water (DW; control), or in 0.5% or 1.0% BAC, and then incubated in simulated body fluid (SBF). Collagen degradation was assessed by quantification of the dry mass loss and the amount of hydroxyproline (HYP) released from hydrolyzed specimens after 1 or 4 wk. Although all groups demonstrated a significant increase in NL after 1 yr, adhesive modified with 0.5% BAC showed stable bond strength after 1 yr (9% decrease) relative to the control (44% decrease). Significantly less HYP release and dry mass loss were observed for both 0.5% and 1.0% BAC relative to the control. This in vitro study demonstrates that BAC contributes to the preservation of resin–dentin bonds for up to 1 yr by reducing collagen degradation.