CSP-procedure-based 600 MPa-grade hot-rolled TRIP steel and fabrication method

The invention discloses CSP-procedure-based 600 MPa-grade hot-rolled TRIP steel. The CSP-procedure-based 600 MPa-grade hot-rolled TRIP steel comprises the chemical element ingredients of, in percentage by weight, 0.14-0.16% of carbon, 0.90-1.20% of silicon, 1.20-1.40% of manganese, 0.07-0.10% of phosphorus, less than or equal to 0.005% of sulphur, 0.015-0.060% of acid soluble aluminium and the balance ferrum and inevitable impurities. The fabrication method of the CSP-procedure-based 600 MPa-grade hot-rolled TRIP steel comprises the following steps of converter smelting, refined smelting, thin plate billet continuous casting, continuous-casting billet soaking, high-pressure water descaling, controlled rolling, controlled cooling and rolling up. The economic C-Si-Mn-P ingredient design is adopted, a metallographic structure is composed of 50-65% of ferrite, 25-40% of bainite and 5-20% of residual austenite; the yield strength is 390-450 MPa, the strength of extension is 600-680 MPa, and the elongation A80 is 28-35%; and the CSP-procedure-based 600 MPa-grade hot-rolled TRIP steel has good high-plasticity matching.