Determination of defects on a processed disc from S355J2 steel

Purpose – A failed disc that was forged from S355J2 round bar was investigated in order to determine the failure route cause. The purpose of this paper is to determine the defects and route cause analysis regarding their origin. Design/methodology/approach – Macroscopic evaluation, microstructure observation using light optical metallography and scanning electron microscopy with EDX analysis were the techniques used to analyse and characterize the defected areas. Findings – Macro-inclusions (up to 850 µm) that correspond to high melting aluminium rich calcium-aluminate particles were detected. Their formation, possibly due to improper calcium treatment during ladle furnace steel refining process might be associated with clogging problems at casting. SEM-EDX analysis revealed whitish spots containing Zr that could be related to submerged entry nozzle (SEN) erosion/breakage. Characteristic is the large size and unusual shape of the traced particles, as well as the presence of low Si, Na, K. The findings ind...