Facile Synthesis of Gold Nanospheres Modified by Positively Charged Mesoporous Silica, Loaded with Near-Infrared Fluorescent Dye, for in Vivo X-ray Computed Tomography and Fluorescence Dual Mode Imaging

We developed a simple and efficient method to synthesize a novel probe for both computed tomography (CT) and fluorescence imaging. Gold nanospheres were coated with positively charged mesoporous silica (Au@mSiO2-TTA) using a one-pot method to cohydrolyze quaternary ammonium silane and tetraethyl orthosilicate. Subsequently, IR-783, a negatively charged and water-soluble near-infrared fluorescent dye, was electrostatically adsorbed into the silica shell. Transmission electron microscopy imaging, X-ray powder diffraction, and energy dispersive X-ray spectroscopy indicated that Au@mSiO2-TTA had a clear core–shell structure, was monodisperse, had a large surface area (530 m2/g), and had a uniform pore size (2.2 nm). The mesoporous structure could effectively load fluorescent dye. After loading, the zeta potential of the nanoparticle dropped from 48 mV to 30 mV, and after additional modification with polyvinylpyrrolidone, it further reduced to 6 mV. Probe fluorescence was stable over time, and the probe was an...