Reduced surface spin disorder in ZrO2 coated γ-Fe2O3 nanoparticles

Abstract Surface spin disorder in microwave plasma synthesized zirconium dioxide (ZrO 2 ) coated maghemite (γ-Fe 2 O 3 ) nanoparticles have been studied by using AC and DC magnetic measurements. The inverse spinel structure of γ-Fe 2 O 3 was confirmed by X-ray diffraction. The calculated average crystallite size of γ-Fe 2 O 3 and ZrO 2 phase was about 13 and 6 nm, respectively. Zero field cooled/field cooled measurements revealed average blocking temperature at 65 K. The fitted value of K eff deduced from simulation was higher than that of bulk γ-Fe 2 O 3 magneto-crystalline anisotropy which is mainly due to surface spin disorder. However, it was lower than the reported value for uncoated γ-Fe 2 O 3 nanoparticles, which is due to reduction in surface effects and interparticle interactions in ZrO 2 coated nanoparticles. Below 25 K, a sharp increase in saturation magnetization was observed which is due to extra contribution of frozen surface spins to magnetism at low temperatures. The coercivity also showed a sharp increase below 25 K, which is due to presence of strong core-surface interactions at low temperatures. For AC susceptibility, Arrhenius law fit revealed weak interactions among the nanoparticles which were not strong enough to create a spin-glass state. In summary, ZrO 2 coated γ-Fe 2 O 3 nanoparticles showed reduced surface spin disorder and weak interparticle interactions which is due to non-magnetic ZrO 2 coating.