Fluorine Gypsum Modification and Preparation of Self-Leveling Material

The fluorine gypsum was used as research object in this paper. In order to recognize the basic properties of fluorine gypsum fully, the physical and chemical properties were analyzed through different testing means. The chemical modification (additive A, sodium sulfate, quick lime) on the activity of fluorine gypsum excitation effect were studied. The best way to compound modification was determined and the mechanism of the admixture was analyzed. On this basis, the fluorine gypsum base self-leveling mortar materials was prepared and its performances were tested. Research shows that, the optimal ratio of: additive A content 2.0% (mixed), sodium sulfate content 0.8%, quick lime content 1.5%, the fluorine gypsum self-leveling material initial setting time is 2.4h, the final setting time is 5.3h, 24h flexural strength of 2.60MPa, compressive strength of 6.05MPa, the dry flexural strength of 7.68MPa, compressive strength of 22.89MPa, the performance indicators have reached the JC/T1023-2007《Gypsum based self-leveling mortar》 requirements.