Enhanced Methane Sensing Properties of WO3 Nanosheets with Dominant Exposed (200) Facet via Loading of SnO2 Nanoparticles

Methane detection is extremely difficult, especially at low temperatures, due to its high chemical stability. Here, WO3 nanosheets loaded with SnO2 nanoparticles with a particle size of about 2 nm were prepared by simple impregnation and subsequent calcination using SnO2 and WO3·H2O as precursors. The response of SnO2-loaded WO3 nanosheet composites to methane is about 1.4 times higher than that of pure WO3 at the low optimum operating temperature (90 °C). Satisfying repeatability and long-term stability are ensured. The dominant exposed (200) crystal plane of WO3 nanosheets has a good balance between easy oxygen chemisorption and high reactivity at the dangling bonds of W atoms, beneficial for gas-sensing properties. Moreover, the formation of a n–n type heterojunction at the SnO2-WO3 interface and additionally the increase of specific surface area and defect density via SnO2 loading enhance the response further. Therefore, the SnO2-WO3 composite is promising for the development of sensor devices to methane.