The Effect of Structure of the Clay Modifier on the Morphology and Properties of Polystyrene/Clay Nanocomposites Prepared via In Situ Suspension Polymerization

Polystyrene (PS)/organoclay nanocomposites were prepared via free radical suspension polymerization. Two kinds of organoclay were used, labeled KT and KD, modified by trimethyloctadecyl ammonium (TM) and dimethyldioctadecyl ammonium (DM) ions, respectively. Nanocomposites containing various amounts of both of the organoclay nanoparticles (1, 3, and 5 wt%) were prepared. The wide angle X-ray diffraction (WAXD) results revealed intercalation in both of the nanocomposites. The greatest improvement in thermal stability of the nanocomposites was achieved with 5 wt% of organo-MMT for both of the clays. The nanocomposite containing 3 wt% of KT organo-MMT showed the greatest improvement of storage modulus. When the organoclay content exceeded 3 wt%, the storage moduli decreased compared to the nanocomposite filled with 3 wt% of the organoclay. D-spacing calculations using Bragg's law and WAXD data showed that the KT and KD nanoparticles were intercalated within the PS matrix, but with different extents of interca...