Effect of PbI2 deposition rate on two-step PVD/CVD all-vacuum prepared perovskite
2016
Abstract In this work we fabricate all-vacuum processed methyl ammonium lead halide perovskite by a sequence of physical vapour deposition of PbI 2 and chemical vapour deposition (CVD) of CH 3 NH 3 I under a static atmosphere. We demonstrate that for higher deposition rate the (001) planes of PbI 2 film show a higher degree of alignment parallel to the sample's surface. From X-ray diffraction data of the resulted perovskite film we derive that the intercalation rate of CH 3 NH 3 I is fostered for PbI 2 films with higher degree of (001) planes alignment. The stoichiometry of the produced perovskite film is also studied by Hard X-ray photoelectron spectroscopy measurements. Complete all-vacuum perovskite solar cells were fabricated on glass/ITO substrates coated by an ultra-thin (5 nm) Zn-phthalocyanine film as hole selective layer. A dependence of residual PbI 2 on the solar cells performance is displayed, while photovoltaic devices with efficiency up to η =11.6% were achieved.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
40
References
22
Citations
NaN
KQI